Material	Grade	Ultimate tensile strength	Hardness	Chemical resistance	Maximum service temperature
Aluminum	6061-T6	291-320 Mpa	60 HRB	High	130-150 °C
	7075-T6	434-580 Mpa	79-86 HRB	Moderate	100 °C
	6063	110-300 Mpa	25-95 HRB	High	—
	7050	500-552 Mpa	147 HB	Good	—
	2024	200-540 Mpa	70-120 HB	Poor	200 °C
Stainless steel	304/304L	480-620 Mpa	75-83 HRB	Good	750-925 °C
	316/316L	480-620 Mpa	75-83 HRB	Excellent	750-925 °C
	303	528-639 Mpa	81-96 HRB	Moderate	750-925 °C
	17-4PH	896-990 Mpa	250-260 HV	Excellent	282-316 °C
Carbon Steel	Low Carbon 1018	190-440 Mpa	76 HRB	Poor	—
	Low Carbon A36	400-550 Mpa	92 HRB	Poor	Variable °C
	Medium Carbon 1045	620-680 Mpa	84 HRB	Poor	—
Copper	Copper C110	220 – 230 Mpa	40 HRF	Moderate to Poor	—
	Copper C101	310 – 380 Mpa	27 HV	—	77-87 °C
Brass	Brass C360	140 Mpa	—	Moderate	—
Titanium	Grade 1	240 Mpa	120 HB	Excellent	320-400 °C
	Grade 2	344-420 Mpa	80-82 HRB	Excellent	320-430 °C