Mate­r­i­al	Grade	Ulti­mate ten­sile strength	Hard­ness	Chem­i­cal resis­tance	Max­i­mum ser­vice tem­per­a­ture
Alu­minum	6061-T6	291–320 Mpa	60 HRB	High	130–150 °C
	7075-T6	434–580 Mpa	79–86 HRB	Mod­er­ate	100 °C
	6063	110–300 Mpa	25–95 HRB	High	—
	7050	500–552 Mpa	147 HB	Good	—
	2024	200–540 Mpa	70–120 HB	Poor	200 °C
Stain­less steel	304/304L	480–620 Mpa	75–83 HRB	Good	750–925 °C
	316/316L	480–620 Mpa	75–83 HRB	Excel­lent	750–925 °C
	303	528–639 Mpa	81–96 HRB	Mod­er­ate	750–925 °C
	17–4PH	896–990 Mpa	250–260 HV	Excel­lent	282–316 °C
Car­bon Steel	Low Car­bon 1018	190–440 Mpa	76 HRB	Poor	—
	Low Car­bon A36	400–550 Mpa	92 HRB	Poor	Vari­able °C
	Medi­um Car­bon 1045	620–680 Mpa	84 HRB	Poor	—
Cop­per	Cop­per C110	220 — 230 Mpa	40 HRF	Mod­er­ate to Poor	—
	Cop­per C101	310 — 380 Mpa	27 HV	—	77–87 °C
Brass	Brass C360	140 Mpa	—	Mod­er­ate	—
Tita­ni­um	Grade 1	240 Mpa	120 HB	Excel­lent	320–400 °C
	Grade 2	344–420 Mpa	80–82 HRB	Excel­lent	320–430 °C